Mg/TF pyrolant is one of the high energy materials and it's ignition delay time characteristics were obtained.
Ignition temperature (Tig) of Mg/TF pyrolants, the concentration of Mg (ξMg) were 60, 70, and 80 wt%, reached between
906 and 921K and over 900K when ignition delay time was 4 seconds. Mg/TF pyrolant is difficult to ignite, so it is easy
and safe to handle. And ignition delay time was measured by heating them with Nichrome wires. Ignition delay time(τig)
is decreased with increasing electric current (I), and τig is proportion to I-2. And also ignition delay time
is increased with increasing the diameter of Nichrome wire (φ) on the constant electric current. So τig is proportion
to φ3.6. And also τig is proportion to input energy E-1.8.
高エネルギ物質であるMg/TFパイロラントの着火遅れ時間特性を求めた。着火温度はクルップ発火点試験装置で測定し,着火遅れ時間が4sのときの着火温度はMgの混合量により異なり，Mgの混合量が60〜80 wt% で906〜921K と900K を超えている。Mg/TF パイロラントは着火温度が高く着火しにくいことから取り扱い上安全であることが得られた。ニクロム線にパイロラントを付着させ着火遅れ時間を測定した。電流を増加すると着火遅れ時間は短くなり，減少量は電流の−2乗に比例することが得られた。着火遅れ時間は線径の3.6乗に比例して増加し,供給エネルギの1.8乗に反比例して減少することが得られた。