Thermal analysis, analysis of the combustion residue and combustion characteristics measurement such
as burning rate or temperature were carried out to clarify the combustion mechanism of a tungsten -
potassium perchlorate - barium chromate delay powder. The results obtained are as follows.
The main reaction of the delay powder of tungsten - potassium perchlorate - barium chromate is the
oxidation of tungsten by potassium perchlorate. Barium chromate acts as a burning rate modifier, and
the smaller the content the larger is the burning rate.
Three types of delay compositions used in this study show characteristic burning behavior.
A stoichiometric or a oxidizer - rich composition has a small linear burning rate, although it has a
large heat of combustion. On the other hand, a tungsten - excess or fuel - rich composition with a
small heat of combustion has a larger linear burning rate than the former, showing a small fractional
oxidation of tungsten (below 10 %) contained in the delay powder. From these results, a surface combustion
mechanism is proposed for the combustion mechanism of this delay powder.
タングステン一過塩素酸カリウム - クロム酸バリウム系延時薬の燃焼機構を明らかにするために, 熱分析, 燃焼残留物の分析および燃焼速度や温度などの燃焼特性値などを測定することにより検討した。 得られた結論は以下の通りである。
タングステン一過塩素酸カリウム - クロム酸バリウム系延時薬の主反応は, 過塩素酸カリウムによるタングステンの酸化である。 クロム酸バリウムは燃焼調整剤として働き, その量が多ければ燃焼速度は小さくなる。 この主反応の等量組成あるいは酸化剤が過剰な組成では燃焼熱は大きいが, 燃焼速度は小さい。これに対して, タングステン（燃料）過剰の組成では燃焼熱は小さいが, 燃焼速度は前者の数倍にもなった。この場合に燃料タングテンの酸化率は非常に小さく, 10 ％以下である。 これらの結果から, この系の燃焼機構として表面燃焼機構が提案された。