This report mainly consists of the measurement result on the pressure distribution from what portions occure by the expansion of the static demolition agent in the aluminum pipe.
As the result, the expansion pressure doesn't occure equally from all portion charged in aluminum pipe but comes out from the particular portion. This section is approximately at 20% areas from bottom of the pipe. In order to examine the above result, two kinds of experiments are taken.
The first, using the opaque plastic tube of which free deformations are capable at any surface, it is observed that any portion of the pipe starts to enlarge toward circular direction.
The second is the test using the opaque acrylic block in order to observe the expansion behavior under the confinement condition.
Both of them are showed the same tendency as the pressure distribution measurement that the expansion stats to occure at 20% around from bottom of the pipe.
Finally, the test of the breacrage properties on lime ston rocks is examined compared with circular holes and elliptical holes.
Consequently, it is found that the spacing of elliptical holes is prolonged 1.6 times than circular holes.
速効性静的破砕剤を円孔に充填し, 注水による水和反応で発生する膨脹圧の深さ方向分布とその時間推移を測定した｡ その結果, 充填された円孔内のすべての位置から均一に圧力は上昇しておらず, 孔底から約20 %上部附近の特定位置から圧力上昇は開始し, 漸次孔全体に亘って広がっていることが判明した。
上記の実証試験としてアクリル製透明パイプに充填した場合の破砕状況, および透明アクリルブロック中で拘束状態下にある破砕剤の応力挙動について観察した｡
その結果, 前者ではパイプ下端から1/4附近より膨脹は開始し, 時間と共に膨脹はパイプ上下方向に推移しパイプ外径は拡大され, 約15分後にはパイプ破断が発生した｡ 一方, 体積膨脹の最終形体が塑性変形として把えることができるアクリルブロック試験では充填孔の中間領域が最も大きく拡張され, 上端および下端領域では孔の拡大は観測されてなかった｡ この二つの実証実験は, 円孔内圧力分布試験結果と概ね一致する結果が得られたものと考える｡
次に, この円孔内において等しい膨張特性を示す破砕剤を用い断面特性の影響, 特に先端き裂効果をみるため穿孔断面が円孔と楕円形状における破砕特性を石灰石岩盤にて評価した｡ その結果, 楕円形状での破砕はき裂発生が長軸方向のみに進行し, かつ最大き裂伝播距離は円孔に対し, 約1.7倍となり長軸方向での応力集中効果が観測された。