Fine ammonium perchlorate (AP) is required in order to prepare a high burning rate AP based composite propellant. Fine hollow AP(FAP), of which the mean volume-surface diameter is about 2.7 μm, is prepared by the spray-drying method. The crystallographical property and the thermochemical behavior of FAP, and the productivity and the burning rate characteristics of the propellant prepared with FAP were investigated in this study. The results were as follows; The crystallographical property and the thermochemical behavior of FAP are almost the same as those of the ground commercial AP (CAP). The upper limit of the FAP content in propellant is 72 wt%. The propellant was prepared at 80 wt% AP with a bimodal AP, FAP and CAP. The burning rate of the propellant contained 80 wt% AP with a bimodal AP, which was different in the relative amounts of FAP and CAP, increases with increasing the content of FAP. The increment of burning rate at high pressures is larger than that at low pressures. It is found that FAP is an effective oxidizer for the increase in the burning rate.
高燃焼速度を有するAP系コンポジット推進薬が要求されている｡ 噴霧乾燥法によって, 体面積平均径2.7μmの微粒な中空過塩素酸アンモニウム(FAP)が調製された｡ 本実験では, FAPの結晶学的性質と熱分解性について調べるとともに, FAPを用いた推進薬の燃焼速度について調べた｡ その結果, 以下のことが明らかにされた｡ FAPの結晶学的性質と熱分解性は, 粉砕された市販のAP(CAP)のそれとほぼ同じであった｡ FAPのみを用いて推進薬を製造した場合, 推進薬に混入できるAP含有率の上限は72 wt%であった｡ FAPの一部をCAPに置き換えることによって, AP含有率8O wt%の推進薬を製造できた｡ AP含有率80 wt%において, FAPとCAPの混合割合を変化させて推進薬を製造したところ, それらの燃焼速度はFAPの混合割合が増加するにしたがい大きくなった｡ 高圧部における燃焼速度の増加量は低圧部のそれより大きかった｡ 以上の結果から, 高燃焼速度のAP / HTPB系コンポジット推進薬を製造するために, FAPは有効な酸化剤であることがわかった｡