Fullerene is a typical nano-carbon material with interesting properties. Though a great deal of research has been performed on the basic properties of fullerene to the present, little thermal research has been reported. This study examined the physical and chemical properties, thermal reactivity, and combustion reactivity of fullerene. The results obtained were as follows. Fullerene is a carbon material with high crystallinity which has higher carbon content compared to the other carbon materials. Fullerene C60 and Mixed fullerene(MF) caused sublimation and suffered oxidation in air at lower temperature compared standard carbon black. And C60 was more thermally stable than MF, which contained higher fullerenes including C70, according to the oxidation reaction in air. Fullerenes burn, while the carbon black does not burn. However, in the burning rate test by the U N ,fullerenes are not a flammable materials.
フラーレンは炭素原子のみからなり，中空構造をもったナノサイズの「炭素分子」である。フラーレンには代 表的なC60 を含め，さまざまな炭素数を持つものが存在し，基礎的な性質についての研究は，現在まで数多くな されているが，熱的な研究報告は少ない。従って，本研究ではフラーレンの物理的，化学的性質と熱反応性及び 燃焼反応性について検討した。 その結果，フラーレンは結晶性の高い炭素材で，標準カーボンブラックに比べて，酸化開始温度が低く、燃焼 速度も速く，熱的な反応性が高い。 また，燃焼速度は粒子径に反比例し速くなるが，粒子径によらず可燃性物質には該当しないことが判った。
Fullerene, Nano-carbon, TG-DTA, Burning test, Inflammability.