It was reported that the curing behavior, mechanical properties, and thermal decomposition behavior of HTPB binder was improved by a small amount addition of polytetrahydrofuran (PTHF) to HTPB. In this study, the curing behavior, mechanical properties and burning characteristics of the AP / HTPB composite propellant using PTHF as a plasticizer. PTHF had a little effect on the hardness of the propellant. The tensile properties were changed by the addition of PTHF and these properties of propellants added with PTHF were not influenced by the AP content and the molecular weight of PTHF. The specific impulse and adiabatic flame temperature are theoretically increased by the use of PTHF as a plasticizer. On the other hand, the thermal decomposition behavior and the burning rates of the AP / HTPB propellant were not improved by the small amount addition of PTHF.
少量のポリテトラヒドロフラン（PTHF）を末端水酸基ポリブタジエン（HTPB）に添加することによって，HTPBの硬化特性，機械的物性と熱分解性を改善できると報告された。本実験では，可塑剤としてPTHFを添加されたAP/HTPB系推進薬の硬化特性，機械的特性と燃焼特性について調べた。PTHFを添加することによって，未硬化推進薬の粘度増加率を低下できることがわかった。推進薬の硬度に対するPTHFの影響は小さかった。引張り特性はPTHFの添加によって変化させることができた。引張り強度と伸びはAP含有率とPTHFの分子量にほとんど依存しなかった。理論的には，推進薬の比推力はPTHFを添加することによって増加できることがわかった。一方，推進薬の熱分解性と燃焼速度は，PTHF添加の影響をほとんど受けなかった。
polytetrahydrofuran, plasticizer, hydroxyl-terminated polybutadiene, composite propellant.